Studi Parametrik Mortar Geopolimer Hybrid Abu Sawit (Palm Oil Fuel Ash/POFA)

Ramadhan Yanuari, Muhammad Ikrammullah, Dinda Septari, Miguel Felix Wijaya, Monita Olivia

Abstract


In this study, the Palm Oil Fuel Ash (POFA) was used as a raw material for making geopolymer mortars that uses a combination of sodium hydroxide (NaOH) and sodium silicate (Na2SiO3). The purpose of this study was to determine the effect of various parameters on the compressive strength of mortars. The parameters involved were namely modulus of activator ratio (Ms 1-3), the molarity of NaOH (10-16M), curing temperature (28-110ºC), type of POFA particle processing (oven-dried, passed the #200 sieve, burned in a brick kiln, burned at 800ºC), rest periods of 3 and 5 days. Based on the parametric study, it was found the optimum mixture with the highest compressive strength consisted of NaOH 14M, Ms ratio of 2.5, curing temperature of 100OC, a rest period of 5 days, particles sieved using #200 sieve and had 15% PCC content. 


Keywords


Palm Oil Fuel Ash (POFA); compressive strength; geopolymer cement; parametric study; portland cement

Full Text:

PDF

References


Laporan Tahunan PT Semen Indonesia (Persero) Tbk. Accelerated Transformation, 2018

Canpolat, B. R. et al. 2001. Emission Factor of Cement Industry in Turkey. Istanbul, Turkey : Kluwer Academic Publisher, 138: 235-252, 2002

Davidovits, J., Properties of Geopolymer Cements, Vol 16, 1994: 1-19

Miranda J. M., Fernandez-Jime A., Gonzalez J. A, dan Palomob A, Corrosion Resistance in Activated Fly Ash Mortars, Vol 137, 2006: 1656-1663

Direktorat Jenderal Perkebunan. Statistik Perkebunan Indonesia, Kelapa Sawit, 2016-2018, 2018

Farandia, Ririn Y., et al. Kinerja Beton High Volume Pofa, Vol 1, 2014: 1-12.

Tangchirapat, W., C. Jaturapitakkul and P. Chindaprasirt, 2009. Use of Palm Oil Fuel Ash as a Supplementary Cementitious Material for Producing High-strength Concrete. Construction and Building Materials, 23(7): 2641-2646.

Olivia, M., Tambunan, L., dan Saputra, E., Properties of Palm Oil Fuel Ash (POFA) Geopolymer Mortar Cured at Ambient Temperature, Vol 97, 2017

Tambunan, L., Olivia, M., dan Saputra, E., Kuat Tekan Mortar Geopolymer POFA yang dirawat pada suhu ruang, Vol 3, 2016

SNI 03-6825-2002, Metode Pengujian Kekuatan Tekan Mortar Semen Portland untuk Pekerjaan Sipil, 2002

SNI 6882-2014, Spesifikasi mortar untuk pekerjaan unit pasangan Standard Specification for Mortar for Unit Masonry, 2014

Davidovits, J., High-Alkali Cements for 21st Century Concretes, Vol 144, 1994: 383-398

Ekaputri, J. J., Analisa Sifat Mekanik Beton Geopolimer Berbahan Dasar Fly Ash Jawa Power Paiton Sebagai Material Alternatif, 2014

Hardjito, D., Wallah, S. E., dan Rangan, B. V., Studies on Engineering Properties of Fly Ash-Based Geopolymer Concrete, Vol 38, 2005: 44-47

Adam, A. Strength and Durability Properties of Alkali Activated Slag and Fly Ash-Based Geopolymer Concrete, 2009: 1-127

Fernandez-Jimenez, A., Palomo, A., dan Criado, M. Microstructure Development of Alkali-Activated Fly Ash Cement: A Descriptive Model, Vol 35, 2005: 1204-1209

Olivia, M., Geopolimer sebagai Material Infrastruktur Berkelanjutan di Lingkungan Gambut, Vol 6, 2015

Mulia., Pemanfaatan Tandan Kosong dan Cangkang Kelapa Sawit Sebagai Briket Arang, 2007

Khalil, M., Y. and Merz, E., Immobolisation of Intermediate Level Wastes in Geopolymer,Vol 211, 1994: 141-148

ASTM C-618 2005, Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use, 2005

Pradana, T., Olivia, M., dan Sitompul, I. R., Kuat Tekan dan Porositas Beton OPC, PCC, dan OPC POFA di Lingkungan Gambut, Vol 3, 2016: 1-8

Tangchirapat, W., Jaturapitakkul, C. dan Chindaprasirt, P., Use of Palm Oil Fuel Ash as a Supplementary Cementitious Material for Producing High-Strength Concrete, Vol 23, 2009: 2641-2646.

SNI 15-2049-2004. Semen Portland, 2004

Kasyanto, H., Tinjauan Kuat Tekan Geopolimer Berbahan Dasar Fly Ash dengan Aktivator Sodium Hidroksida dan Sodium Silikat, 2012

Utami, R. I. A., dan Herbudiman, B., Efek Tipe Superplasticizer Terhadap Sifat Beton Segar dan Beton Keras pada Beton Geopolimer Berbasis Fly Ash, Vol 3, 2017: 1-12

SNI 03-1968-1990, Metode Pengujian Tentang Analisis Saringan Agregat Halus dan Kasar, 1990

SNI 7974-2013, Spesifikasi Air Pencampur yang Digunakan dalam Produksi Beton Semen Hidraulis, 2013

Steveson, M. dan Sagoe-Crentsil, K., Relationships Between Composition, Structure and Strength of Inorganic Polymers, Vol 40, 2005: 2023-2036

Sindhunata, Provis, J.L., Lukey, G.C., Xu, H., and van Deventer, J.S.J, Structural Evolution of Fly Ash Based Geopolymers in Alkaline Environments, Vol 47, 2008: 2991-2999

Rangan, B. V., Hardjito, D., Wallah, S. E., & Sumajouw, D. M. J., Fly ash based geopolymer concrete: a construction material for sustainable development, Vol 31, 2005: 25-30

Johari, M., A., M., Zeyad, A., M., Bunnori N., M., dan Ariffin, K., S., Properties of High-Strength Green Concrete Containing High Volume of Ultrafine Palm Oil Fuel Ash, Vol 30, 2012: 281-288

Salih, M. A., Ali, A. A. A., and Farzadnia, N., Characterization of Mechanical and Microstructural Properties of Palm Oil Fuel Ash Geopolymer Cement Paste, Vol 65, 2014: 592-603


Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.